沙特创新 美国GE PC 940A-116 沙特创新 美国GE PC 940A-116原料描述部分
| 规格级别 | 注塑级 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 特性：中粘度 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | --- | ASTM D-570 | 0.15 | % | |
| 熔体流动速率 | --- | ASTM D-1238 | 7 | g/10min | ||
| 物理性能 | 比重 | --- | ASTM D-792 | 1.21 | --- | |
| 阻燃性 | --- | UL 94 | 1.6 | mm | ||
| 阻燃性 | --- | UL 94 | V-2 | --- | ||
| 模具收缩率 | 3.2mm | ASTM D-955 | 5-7 | 10-3 | ||
| 阻燃性 | --- | UL 94 | 3.0 | mm | ||
| 阻燃性 | --- | UL 94 | V-0 | --- | ||
| 机械性能 | 缺口冲击强度 | 23℃ | ASTM D-256 | 640 | J/m | |
| 弯曲模量 | --- | ASTM D-790 | 3250 | MPa | ||
| 拉伸强度 | 屈服点 | --- | ASTM D-638 | 62 | MPa | |
| 断裂点 | --- | ASTM D-638 | 56 | MPa | ||
| 断裂伸长率 | --- | ASTM D-638 | 90 | % | ||
| 弯曲强度 | --- | ASTM D-790 | 91 | MPa | ||
| 洛氏硬度 | --- | ASTM D-785 | 118 | --- | ||
| 电气性能 | 介电常数 | 1MHz | ASTM D-150 | 2.96 | --- | |
| 损耗因数 | 1MHz | ASTM D-150 | 0.01 | --- | ||
| 损耗因数 | 60Hz | ASTM D-150 | 0.0009 | --- | ||
| 介电常数 | 60Hz | ASTM D-150 | 3.01 | --- | ||
| 体积电阻率 | --- | ASTM D-257 | 1.0×1017 | Ω.cm | ||
| 热性能 | 热变形温度 | 0.45MPa | ASTM D-648 | 137 | ℃ | |
PC(聚炭酸酯)：(1)日本出光:A2200 、G2520、G3030、G2510、LC1500、LC1700、IR2200 (2)日本三菱：7022IR、7025IR、7030IR、S3000、S2000、GSV2020、GSV2030、7025G10、7025G20、7025G20I、7027R、7025GR1120、GS2010MLR、GSH2010MR2、GSH2020R2、GS2030MR2、GSN2020KR、GS2020MLR、GS2010MPH、 (3)日本帝人：1250Y、1225Y、2225Y、3420、3430、1225L、LS-2030、GN3130、G3110H、GN3410、G3330 (4)德国拜耳：2205、2207(高流动)、2405、2407(抗UV)、2458、6265、2605、2607、2658、2665、2667、2805、2807(抗UV)、2858、2865、2867、6555、6585、6557、6465、6485、9125,GF20、9415、GF10、3103、3105、3107、3108、3158、3208(耐冲高粘)、9425,GF30、OD2015、LQ3147、AL2647、RX-1805、1243、1239(吹瓶专用料) (5)美国GE：141R、241R、243、223、143、940A、945A、925、3410R、3412R、3413R、3414R、121R、221R、103R、203R、123R、134R、194R、104R、124R、224R、920、923A、943A、953A、HF1110、HF1110R、HF1130、HF1140、QQ4120R、QQ4320R、QQ2320、QQ1020L、EXL1414